Manganese oxide planetary milling: D90 = 1 µm at six hours
Manganese oxide planetary milling: D90 = 1 µm at six hours. The recorded fineness requirement was 1 µm; no all-particle condition was stated.
Sample trials.
Explore the material, the setup and the measured result.
117 sample trials
View record
Ceramic wet milling: two recorded refinement sequences ending at 0.8 µm
Ceramic wet milling: two recorded refinement sequences ending at 0.8 µm. Observe the grinding response; no numerical acceptance criterion was recorded.
Barium titanate wet milling: recorded D50 0.5 and D90 0.7 at two hours
Barium titanate wet milling: recorded D50 0.5 and D90 0.7 at two hours. Meet a recorded 0.8 µm fineness requirement; the target statistic was not specified.
Molybdenum–chromium alloy: observed refinement over a fifteen-hour planetary trial
Molybdenum–chromium alloy: observed refinement over a fifteen-hour planetary trial. Observe the material response; no numerical particle-size target was entered.
Silver powder wet planetary milling: a recorded 500-mesh endpoint at sixteen hours
Silver powder wet planetary milling: a recorded 500-mesh endpoint at sixteen hours. Meet the stated 500-mesh requirement.
Pollen planetary milling: initial grains followed by recorded acceptance at three hours
Pollen planetary milling: initial grains followed by recorded acceptance at three hours. Observe the response and obtain an acceptable milled sample; no numerical target was entered.
Slurry trial meeting a 300-mesh check after three hours in steel equipment
Slurry trial meeting a 300-mesh check after three hours in steel equipment. Meet the recorded 300-mesh requirement.
Silica wet planetary trial recorded as meeting a 600-mesh requirement
Silica wet planetary trial recorded as meeting a 600-mesh requirement. Meet the stated 600-mesh requirement.
Iron ore planetary trial recorded as meeting a 600-mesh requirement
Iron ore planetary trial recorded as meeting a 600-mesh requirement. Meet the recorded 600-mesh requirement.
Slurry planetary milling: complete passage through a 300-mesh sieve at three hours
Slurry planetary milling: complete passage through a 300-mesh sieve at three hours. Make the sample finer; the reported practical check was a 300-mesh sieve.
Pigment powder accepted after three hours without adhesion
Pigment powder accepted after three hours without adhesion. Observe milling behavior and obtain an acceptable sample; no numerical fineness target was entered.
Pharmaceutical powder: an accepted one-hour horizontal planetary observation
Pharmaceutical powder: an accepted one-hour horizontal planetary observation. Make the powder finer; no numerical endpoint was specified.
Results apply to the sample and conditions tested. Review each record for its setup and measurement notes.