Iron-oxide magnetic microspheres: a recorded 2.5 µm result after ninety minutes
Iron-oxide magnetic microspheres: a recorded 2.5 µm result after ninety minutes. Reach below 3 µm.
Sample trials.
Explore the material, the setup and the measured result.
117 sample trials
View record
Pseudoboehmite wet planetary trial: recorded refinement to 1 µm at eight hours
Pseudoboehmite wet planetary trial: recorded refinement to 1 µm at eight hours. Meet the stated 1 µm requirement.
Alumina wet planetary trial: a recorded change from 33 to 13 µm in thirty minutes
Alumina wet planetary trial: a recorded change from 33 to 13 µm in thirty minutes. Reach a recorded 13 µm endpoint.
Coating-material dispersion trial accepted after twenty minutes
Coating-material dispersion trial accepted after twenty minutes. Break up agglomerates and obtain an even dispersion.
Magnetic powder: complete 325-mesh sieve passage after four hours
Magnetic powder: complete 325-mesh sieve passage after four hours. Meet the 325-mesh requirement using a sieve measurement.
Activated carbon: a recorded thirty-minute 200-mesh outcome
Activated carbon: a recorded thirty-minute 200-mesh outcome. Meet the stated 200-mesh requirement.
Tea-leaf planetary trial with a recorded two-hour 200-mesh result
Tea-leaf planetary trial with a recorded two-hour 200-mesh result. Meet the recorded 200-mesh requirement.
Tea leaves: a recorded 200-mesh result after two hours
Tea leaves: a recorded 200-mesh result after two hours. Meet the stated 200-mesh requirement.
Hair planetary trial recorded as meeting an 80 µm requirement at two hours
Hair planetary trial recorded as meeting an 80 µm requirement at two hours. Meet the stated 80 µm fineness requirement.
Boron oxide: a favorable argon-filled horizontal planetary trial
Boron oxide: a favorable argon-filled horizontal planetary trial. Observe the milling response; no numerical fineness criterion was entered.
Soil planetary preparation: a recorded five-minute 100-mesh observation
Soil planetary preparation: a recorded five-minute 100-mesh observation. Observe sample preparation behavior; no numerical acceptance target was entered.
Coal preparation: pre-crushing followed by a twenty-minute planetary mesh result
Coal preparation: pre-crushing followed by a twenty-minute planetary mesh result. Observe milling behavior and obtain a useful finer product; no separate numerical target was entered.
Results apply to the sample and conditions tested. Review each record for its setup and measurement notes.